Effect of basalt addition on tribological performance of FeCrSiB HVOF coatings; pp. 211–220Full article in PDF format
| doi: 10.3176/eng.2012.3.06
Products made of basalt are recently gaining sufficient attention due to depletion of raw materials serving as reinforcement for construction, and wear resistant materials. Basalt has sufficient mechanical strength, high hardness, low density and superior corrosion resistance. Basalt and other minerals are used in thick metal coatings to adjust their thermal expansion to that of the steel substrate. High velocity oxygen fuel (HVOF) sprayed coating method allows to prepare solid basalt-steel composite materials since the melting temperatures of basalt and steel are very close and materials obtained by casting or sintering will have low mechanical properties. The aim of the current work is to study the change in tribological response under erosive, abrasive, reciprocal and continuous sliding conditions when basalt is added to the harder matrix. It was found that the addition of 12 vol% of basalt to the FeCrSiB HVOF sprayed coating is generally unfavourable in tribological conditions due to the brittleness of basalt and its flake shape. The worst relative performance was observed in reciprocal sliding conditions and the best one in mild conditions of continuous sliding. Discussion on the mechanisms of materials performance is based on SEM and EDS results.
1. Singh, M., Modi, O. P., Dasgupta, R. and Jha, A. K. High stress abrasive wear behaviour of aluminium alloy–granite particle composite. Wear, 1999, 233–235, 455–461.
2. Czigány, T. Basalt fiber reinforced hybrid polymer composites. Mater. Sci. Forum, 2005, 473–474, 59–66.
3. Cao, S., Liu, H., Ge, S. and Wu, G. Mechanical and tribological behaviors of UHMWPE composites filled with basalt fibers. J. Reinf. Plast. Compos., 2011, 30, 1–9.
4. Todic, A., Nedeljkovic, B., Cikara, D. and Ristovic, I. Particulate basalt–polymer composites characteristics investigation. Mater. Des., 2011, 32, 1677–1683.
5. Akinci, A., Ercenk, E., Yilmaz, S. and Sen, U. Slurry erosion behaviors of basalt filled low density polyethylene composites. Mater. Des., 2011, 32, 3106–3111.
6. Märkisches Werk, Crystal coat – an impermeable mineral-metal multiphase coating. http://www.mwh.de/Innovation/Innovations/MWH_CrystalCoat_CC_200.aspx (accessed online 05/05/2012).
7. Dietrich, M., Verlotski, V., Vaßen, R. and Stöver, D. Metal-glass based composites for novel TBC-systems. Mat.-wiss. u. Werkstofftech., 2001, 32, 669–672.
8. Antonov, M., Hussainova, I., Veinthal, R. and Pirso, J. Effect of temperature and load on three-body abrasion of cermets and steel. Tribol. Int., 2012, 46, 261–268.
9. Antonov, M., Hussainova, I., Pirso, J. and Volobujeva, O. Assessment of mechanically mixed layer developing during high temperature erosion of cermets. Wear, 2007, 263 (7–12), 878–886.
10. Michalczewski, R., Antonov, M., Vlad, M., Szczerek, M. and Hussainova, I. The assessment of the coated elements behaviour before and after scuffing under four-ball lubricated testing conditions. In Proc. 2nd European Conference on Tribology ECOTRIB. Pisa, Italy, 2009, 107–112.
11. Szczerek, M., Michalczewski, R. and Piekoszewski, W. The problems of application of PVD/CVD thin hard coatings for heavy-loaded machine components. In Proc. ASME/STLE International Joint Tribology Conference. Miami, Fl, 2008, 35–37.
12. Antonov, M. and Hussainova, I. Cermets surface transformation under erosive and abrasive wear. Tribol. Int.
, 2010, 43
, 1566–1575. http://dx.doi.org/10.1016/j.triboint.2009.12.005Back to Issue