Influence of steel austenitization to part quality in continuous austempering; pp. 221–231

Full article in PDF format | doi: 10.3176/eng.2012.3.07

Authors
Karli Jaason, Priidu Peetsalu, Mart Saarna, Priit Kulu, Valdek Mikli, Liina Lind, Jüri Beilmann

Abstract

In the automotive industry, the heat treatment of strip steel safety components is a crucial and highly responsible process in terms of quality. The growing demand for passenger car safety makes heat treatment highly important in qualified engineering. This study is focused on the part austenitization in the industrial furnace. The study includes testing with a laboratory furnace and an industrial test on a continuous austempering line. The purpose of this work is to find the basis for selecting optimal furnace parameters for the heat treatment line furnace without affecting the final quality of treated parts. For this study, the safety belt tongue, as the main product of the involved company, was chosen. Seatbelt tongues are fineblanked from steel grade C60E, which is preferred for austempering, to gain the desired lower bainitic structure. The results of the study show that the austenitization of the parts depends on the furnace temperature, heating time, layer thickness and the geometry of parts. All these variables affect the final quality of the tongue.


References

1. ASM International Handbook, Heat Treating, vol. 04. ASM International, 1991.

2. Totten, G. E. (ed.). Steel Heat Treatment Handbook, Chapter 2 – Classification and Mechanisms of Steel Transformation. ASM International, 2006.

3. Peetsalu, P., Mikli, V., Ratas, K., Kulper, E. and Jaason, K. Bainitic structure effect on hydrogen embrittlement. J. Japan Soc. Heat Treatment, 2009, 49, 592–595.

4. Totten, G. E. (ed.). Steel Heat Treatment Handbook, Chapter 6 – Steel Heat Treatment. ASM International, 2006.

5. Oliveira, F. L. G., Andrade, M. S. and Cota, A. B. Kinetics of austenite formation during continuous heating in a low carbon steel. Mater. Char., 2007, 58, 256–261.
http://dx.doi.org/10.1016/j.matchar.2006.04.027

6. Katsamas, A. I. A computational study of austenite formation kinetics in rapidly heated steels. Surface Coating Technol., 2007, 201, 6414–6422.
http://dx.doi.org/10.1016/j.surfcoat.2006.12.014

7. Oriani, R. A., Hirth, J. P. and Smialowski, M. Hydrogen Degradation of Ferrous Alloys. William Andrew Publ., Noyes, NJ, 1985.

8. ASM International Handbook, Metallography and Microstructures, vol. 09. ASM International, 1991.

9. Alaa, A. H. and Mohamed, S. H. Modeling of heat treatment of randomly distributed loads in multi-zone continuous furnaces. Mater. Proc. Technol., 2012, 706–709, 289–294.


Back to Issue